Used in automotive OEM coatings; motorcycle topcoats; high-demand plastic paint; two-component PU varnish for various metals and plastics; repair coatings
Chat Now Download TDSDescription
L-1254 is a high-solids, high-hydroxyl-content acrylic copolymer with excellent fast-drying performance (can be polished and sanded at room temperature after 3.5 hours). It exhibits excellent application properties, high build, and is suitable for clear topcoats. The product meets the latest VOC requirements for spray coatings.
Technical data
| Appearance | Colorless transparent liquid |
|---|---|
| Viscosity (25ºC, CPS) | 6,000 - 12,000 |
| Solid content % | 75±2 |
| OH value (solid) | 119 mgKOH/g |
| OH % (solid) | 3.6 |
| Acid value (solid) | 10-16 mgKOH/g |
| Solvent | Butyl ester |
Product Features
High build, high gloss, excellent leveling
Quick drying, can be polished after 3.5 hours at room temperature
Good resistance to gasoline and chemicals
Low VOC content
Reference Formula
| Varnish | Thinner | ||
|---|---|---|---|
| L-1254 resin | 80 | Xylene | 45 |
| T-12 (drier) | 0.1 | Ethyl Acetate | 20 |
| Lencolo 3160 | 0.4 | Butyl Acetate | 25 |
| Lencolo 3108 | 0.2 | PMA | 10 |
| Lencolo 8531 | 0.3 | ||
| Thinner | 19 |
Curing agent (N3390) : Butyl ester = 60 : 40
Main agent : Curing agent : Thinner =2 : 1 : (0.5~1)
Applications
Automotive OEM coatings; motorcycle topcoats; high-demand plastic paint; two-component PU varnish for various metals and plastics; repair coatings
Storage
To prevent premature polymerization due to the high reactivity of this product, keep it tightly sealed and store away from heat sources and direct sunlight. It is recommended to maintain storage temperature below 30 °C. Unused product should be promptly resealed and must not be left open. Under ventilated conditions at 25 °C, the product has a safe storage period of 6 months. Available packaging: 20 kg / 25kg / 200 kg per drum
Tips: L-1254 has low VOC content, high leveling, high build, high gloss, and quick drying.
Related Products
| Product | Description |
|---|---|
| L-1200A | Good Adhesion PU Resin |
| L-1200B | Good Adhesion PU Resin for Inks |
| L-1201 | High Solid Content PU Primer Resin |
| L-1202 | PU Primer Resin for Nylon-reinforced Substrates |
| L-1250 | PU Resin for Metal Paints |
| L-1251 | RCA Resistant PU Resin |
| L-1253 | High Solid Content PU Resin |
| L-1254 | Fast Drying High Solid Content PU Resin |
| L-1255 | High-Gloss Black One-Coat PU Resin |
| L-1256 | Fast Drying High Hydroxyl PU Resin |
| L-1257 | High Weather-resistant & High Build PU Resin |
| L-1258 | High Gloss & High Leveling PU Resin |
| L-1260 | PU Resin for Optical Coating |
| L-1380 | High Flexibility Polyester Resin |
Note: Technical data represents typical values only. In view of the differences in formulas, production process, conditions, all the above statements must be adjusted according to the actual situation, our company does not make any promises. Our company reserves the right to reform its products without prior notice of any changes.
Contact Person: Yuki
Tel: +86 18027002837(WhatsApp)
Email: service@lencolo37.com